5CrNiMo

2019-10-31
5CrNiMo
详细介绍:

5CrNiMo钢具有良好的韧性、强度和高耐磨性,属热作模具钢。它在室温和500~600℃时的力学性能几乎相同。在加热到500℃时,仍能保持住HB300左右的硬度。由于钢中含有钼,因而对回火脆性并不敏感。从600℃缓慢冷却下来以后,冲击韧性仅稍有降低。


化学成份


碳 C :0.50~0.60

硅 Si:≤0.40

锰 Mn:0.50~0.80

硫 S :≤0.030

磷 P :≤0.030

铬 Cr:0.50~0.80

镍 Ni:1.40-1.80

铜 Cu:允许残余含量≤0.30

钼 Mo:0.15~0.30


硬度:退火,241~197HB,压痕直径3.9~4.3mm


技术参数


淬火后 :58

淬火温度℃ :830~860

交货状态 :退火HB≤241

冷却剂 :油Oil


自由锻件公司哪家好,就找唐山盛通锻造有限公司。


5CrNiMo steel has good toughness, strength and high wear resistance, and is a hot work die steel. It has almost the same mechanical properties at room temperature and 500 to 600 °C. When heated to 500 ° C, it can still maintain the hardness of HB300. Because steel contains molybdenum, it is not sensitive to temper brittleness. After slowly cooling from 600 ° C, the impact toughness was only slightly reduced.


chemical composition


Carbon C: 0.50~0.60

Silicon Si: ≤ 0.40

Mn: 0.50 to 0.80

Sulfur S :≤0.030

Phosphorus P :≤0.030

Chromium Cr: 0.50~0.80

Nickel Ni: 1.40-1.80

Copper Cu: Allowable residual content ≤ 0.30

Molybdenum Mo: 0.15~0.30


Hardness: Annealed, 241 ~ 197HB, indentation diameter 3.9 ~ 4.3mm


technical parameter


After quenching: 58

Quenching temperature °C: 830 ~ 860

Delivery status: Annealing HB≤241

Coolant : Oil Oil